Stirling, Seaglade (P092)

Application:
Upholstery fabric
Composition:
70% Polypropylene, 30% wool
Width:
140cm Tolerance ±2%
Weight:
385gms/m2 Tolerance ±5%
Abrasion:
Tested in accordance with BS 5690: 1999 as modified by Annex F of BS 2543: 2004 to 90,000 rubs Martindale.
Meets the requirements of BS 2543: 2004 and has been graded ′SEVERE CONTRACT′ suitable for all types of upholstery use.
Flame Retardancy:
BS 7176: 2007 Low Hazard.
BS EN 1021 - 1: 2006 (Cigarette).
BS EN 1021 - 2: 2006 (Match).
Note: Flammability performance is dependant on foam used.
Light Fastness:
5+ (ISO 105 - B02: 1999)
Fastness to Rubbing:
Wet: 4+ Dry:4+ (ISO 105 - X12:2002)
Colour Matching:
Batch by batch variations in shade may occur within commercial tolerances. We recommend that fabric be examined before use as no claims will be considered after cutting.
Product Development:
We reserve the right to change the specification of our products in line with our product development program without notice.
Fabric Care And Maintenance:
Clean using a proprietary upholstery shampoo. Please refere to our fabric care guide.
Availability:
All our fabrics are generally available ex-stock for immediate despatch.
Technical Assistance:
Our technical staff will be pleased to offer advice on F.R and other matters.
Guarantee:
Fabric guaranteed for 5 years under normal wear and tear. See our Terms and Conditions.

Add to Swatch

Select this option to add this fabric to a downloadable swatch.

Download image

Download a high quality image of this fabric.

Zoom Swatch

Click to see a larger sample of this fabric.

Email Swatch

Email this page to a friend.

· Latest News

CAMIRA UPDATE August 2017   From 1st August please can you contact info@camirafabrics.com for any sample requests, for further information on the almalgamation between Bradbury Fabrics and Camira Fabrics please log on to www.camirafabrics.com/bradbury... read the full story